Delivering High Quality API 5L X52 X56 X60 X65 and X70 Pipe
Email :sales@mahmetal.com
An ISO 9001 | ISO 14001| OHSAS 18001 | PED-97/23/EC | EIL | IBR Certified and Approved Pipes Supplier
API 5L Grade B, X42, X46, X52, X56, X60, X65, X70 PSL1 / PSL2 Sour Service Seamless Line Pipes.
API 5L Grade B, X42, X46, X52, X56, X60, X65, X70 PSL1 / PSL2 HIC Pipes Certified and Tested in accordance with ISO 3183, ISO 15156, NACE MRO175 / 103, HIC, SWC, SSC, SSCC, SOUR SERVICE, H2S, IMPACT, Post Weld Heat Treatment (PWHT), IBR, High yield, IPS-M-PI-190 etc.
MAH Metal Inc is World Renowned Supplier of API 5L PSL2 Pipes, API 5L GRADE B, X42, X46, X52, X56, X60, X65, X70 PSL2 Sour Service Seamless Line Pipes. Among the Largest Stockist & Stockholder of API 5L GRADE B, X42, X46, X52, X56, X60, X65, X70 PSL2 Sour Service Line Pipes in India. Leading Exporter of API 5L GRADE B, X42, X46, X52, X56, X60, X65, X70 PSL2 Sour Service Line Pipes in Integrated Partnership with Top API 5L GRADE B, X42, X46, X52, X56, X60, X65, X70 PSL1 / PSL2 Sour Service Seamless Line Pipes Manufacturers. Genuine Dealer of API 5L LINE PIPEs in USA, European and Japanese Origins. We are the Prominent Trusted Source for API 5L GRADE B, X42, X46,
X52, X56, X60, X65, X70 PSL2 Sour Service Seamless Line Pipes to be used in World Class Projects. we are the Top EPC Contractor's First Choice for API 5L GRADE B, X42, X46, X52, X56, X60, X65, X70 PSL2 Sour Service Seamless
Line Pipes with High Ready Stock Inventory above 20000 Metric Tons.
API 5L GRADE B, X42, X46, X52, X56, X60, X65, X70 PSL1 / PSL2 SOUR SERVICE LINE PIPES
Grades: B, X42, X46, X52, X56, X60, X65, X70, PSL2 SOUR Service / ISO 3183 L245, L290, L320, L360, L390, L415, L450, L480 PSL2 SOUR Service
MAH Metal Inc., we carry a full inventory of
API 5L Sour Service Pipe Carbon Steel Pipe products in a variety of sizes to meet the structural piping requirements for applications the water, petroleum, oil & gas and other industries.
API 5L Sour Service Seamless Pipe Carbon Steel Pipe can be Structural in Nature
or used in Fluid, Gas, Oil Transmission.
MAH Metal Inc. specializes in API 5L Sour Service Seamless Line Pipe
with years of Experience in Manufacturing API 5L Sour Service Carbon Steel Pipe we offer high quality, lower cost but the best service. As a result to that our API 5L Sour Service Pipes export account today is in various countries like Iran, Iraq, Kuwait, Saudi Arabia, Oman, UAE, Singapore, Malaysia, Indonesia, South korea, Chile, Peru, Venezuela, Australia, Nigeria, Angola, Senegal, Mozambique, Algeria, Libya, Azerbaijan, Netherlands, Brazil, Norway, United Kingdom, Mexico, Canada etc.
Seamless API 5L PSL 2 Sour Service Line Pipe for dependable transmission of oil and gas to any type of collection and distribution point
This API 5L specification Covers Seamless and Welded Steel Line Pipe. It includes standard-weight and Extra-Strong threaded Line Pipe. It includes standard-weight and extra-strong threaded line pipe; and standard-weight plain-end, regular-weight plain-end, special plain-end, extra-strong plain-end, special plain-end, extra-strong plain-end pipe; as
as well as bell and spigot and through-the-flow line(TFL) pipe.
The purpose of this specification is to provide standards for pipe suitable for use in conveying gas, water, and oil in both the oil and natural gas industries
Grades covered by this specification are A25 ,A ,B (and the following "X" Grades), X42, X46, X52, X56, X60, X65, X70, X80. The two digit number following the "X" indicates the Minimum Yield Strength (in 000's psi) of pipe produced to this grade.
API 5L Line Pipe can be either seamless or welded. Applications for API 5L include, but are not limited to: petroleum, petrochemical, natural gas industries, and waterworks.
API 5L Line Pipe is dimensionally equivalent to A106 and A53 pipe, conforming to industry standard sizes , however it performs to different mechanical properties. One key defining characteristic of this pipe is its yield strength, where the two digit number following the pipe’s "X" grade indicates the Minimum Yield Strength (in 000's psi) of pipe produced to this grade (i.e. X52 Pipe).
MAH Metal Inc., is a Pipe Distributor in Middle East, Far East and Africa Region that provides API 5L line pipe from 1/2" to 64" in diameter, in grades X42, X46, X52, X60, X65, & X70.
MAH Metal Inc. Supply a full range of API 5L Seamless Pipes in PSL-1 & PSL-2 line pipe.
Hydrogen-Induced Cracking (HIC) Test, NACE TM0284
IC test to evaluate the resistance of pipeline and pressure vessel plate steels to ydrogen Inducted Cracking caused by hydrogen absorption from aqueous sulfide corrosion. An unstressed test specimen is exposed to a solution at ambient temperature and pressure and after a specified time, the test
specimen is removed and evaluated.
Specimen Size
To conduct the HIC test, requires the following sample sizes:
Pipe - upto 2" OD - 200mm long
If the pipe is more than 2" OD pipe - 100mm long sample size is required
Number of pieces to be tested upto 88mm thick/dia - set of 3 pieces to be tested
Number of pieces to be tested more than 88mm thick/dia - 5 pieces to be tested
NACE TM0284 Test Solution
NACE TM0284 specifies either Solution A or Solution B. Solution A is acidified brine. Solution B is simulated seawater prepared in accordance with ASTM D1141.52. In either case, H2S is bubbled through the solution constantly throughout the test period. NACE TM0284 specifies test duration of 96 hours.
Detailed Report
A detailed written report upon completion of each test. Each report includes a description of the test sample that was received, the test procedure that was used, and the pH values of the test solution before exposure and after the exposure. The test bars are cut into sections and examined under a microscope for hydrogen-induced cracks. The dimensions of any such cracks are recorded and used to compute the values in percentage for Crack
Length Ratio (CLR), Crack Thickness Ratio (CTR) and Crack Sensitivity Ratio (CSR).
Our API 5L Sour Service SEAMLESS LINE PIPE range
API 5L Sour Service Pipe Specification
API 5L / ISO 3183 Hot Rolled.
API 5L Sour Service Pipe Grades
API 5L GRADE B PSL1, PSL 2 / API 5L X42 PSL1, PSL 2 / API 5L X46 PSL1, PSL 2 / API 5L X52 PSL1, PSL 2 / API 5L X56 PSL1, PSL 2 / API 5L X60 PSL1, PSL 2 / API 5L X65 PSL1, PSL 2 / X70 PSL1, PSL 2 / API 5L X70 PSL1 / PSL2 / API 5L X80 PSL1, PSL 2 / ISO 3183 L245 PSL1, PSL 2, ISO 3183 L290 PSL1, PSL 2, ISO 3183 L320 PSL1, PSL2, ISO 3183 L360 PSL1, PSL 2, ISO 3183 L390 PSL1, PSL 2, ISO 3183 L415 PSL1, PSL 2, ISO 3183 L450 PSL1, PSL 2, ISO 3183 L485 PSL1, PSL 2
API 5L Sour Service Pipe Type
Seamless
API 5L Sour Service Pipe Outer Diameter Size
3/8" NB To 30" NB (Nominal Bore Size)
API 5L Sour Service Pipe Wall Thickness
Schedule 20 To Schedule XXS (Heavier On Request) Up to 250 mm Thickness
API 5L Sour Service Pipe Length
5 To 7 Meters, 09 To 13 Meters, Single Random Length, Double Random Length And Customize Size.
API 5L Sour Service Pipe Ends
Plain Ends / Beveled Ends / Coupling
API 5L Sour Service Pipe Delivery Conditions
As Rolled, Normalizing Rolled, Thermomechanical Rolled / Formed, Normalizing Formed, Normalized and Tempered / Quenched and Tempered - BR / N / Q /T
API 5L Sour Service Pipe Material Test Certificate
Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab./ Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC
Annex H
(normative)<
PSL 2 Pipe Ordered for SOUR Service
H.1 Introduction
This annex specifies additional provisions that apply for PSL 2 pipe that is ordered for sour service [see 7.2 c) 51 ] .
NOTE The consequences of sudden failures of metallic components used for the oil and gas production associated with their exposure to H2S- containing production fluids led to the development of NACE MR0175/ISO 15156-1[21] and subsequently EFC publication 16[13] ISO 15156-2 used those sources to provide requirements and recommendations for materials qualification and selection for application in environments containing wet H2S in oil and gas production systems. Carbon and low alloy steels selected using ISO 15156—2 are resistant to cracking in defined H2S containing environments in oil and gas production but are not necessarily immune to cracking under all service conditions. Different service conditions might necessitate the alternative testing that is dealt with in ISO 15156—2:2003, Annex B. That annex specifies requirements for qualifying carbon and low alloy steels for H2S service by laboratory testing.
It is the purchaser’s responsibility to select the carbon and low-alloy steels suitable for the intended service.
H.2 Additional information to be supplied by the purchaser
in addition to items a ) to g) as specified by 7.1, the purchase order shall indicate which of the following provisions apply for the specific order item:
a ) steel casting method for strip or plate used for the manufacture of welded pipe (see H.3.3.2.1);
b ) ultrasonic inspection of strip or plate for laminar imperfections (see H.3.3.2.4);
c ) supply of helical-seam pipe containing strip/plate end welds (see H.3.3.2.5);
d ) chemical composition for intermediate grades (see H.4.1.1);
e ) chemical composition for pipe with t > 25,0 mm (0.984 in) (see H.4.1.2);
f ) chemical composition limits (see Table H.1, footnotes c), d,) e), f), i), j)and k);
g ) frequency of hardness testing of the longitudinal seam weld of HFW or SAW pipe (see Table H.3);
h ) SSC test for manufacturing procedure qualification (see Table H.3);
i ) alternative HIC/SWC test methods and associated acceptance criteria (see H.7.3.1.3);
j ) photomicrographs of reportable HIC cracks (see H.7.3.1.4);
k ) alternative SSC test methods and associated acceptance criteria for manufacturing procedure qualification (see H.7.3.2.2);
l ) for pipe with t ≥ 5,0 mm (0.197 in), ultrasonic inspection for laminar imperfections with in extended length of 100 mm (4.0 in ) at the pipe ends (see K.2.1.3 );
m ) magnetic particle inspection for laminar imperfections at each pipe end face/bevel (see K.2.1.4);
Chemical requirement for Sour Service pipes
Table H.1 ---Chemical composition for pipe with t ≤25,0 mm (0.984 in)
Steel grade
Mass fraction, based upon heat and product analyses
%
maximum
Carbon
equivalent a
%
maximum
C b
Si
Mn b
P
S
V
Nb
Ti
Other c, d
CE llw
CE pcm
SMLS and welded pipes
L245NS or BNS
0,14
0,40
1,35
0,020
0,003 e
f
f
0,04
g
0,36
0,19 h
L290NS or X42NS
o,14
0,40
1,35
0,020
0,003 e
0,05
0,05
0,04
-
0,36
0,19 h
L320NS or X46NS
0,14
0,40
1,40
0,020
0,003 e
0,07
0,05
0,04
g
0,38
0,20 h
L360NS or X52NS
0,16
0,45
1,65
0,020
0,003 e
0,10
0,05
0,04
g
0,43
0,22 h
L245QS or BQS
0,14
0,40
1,35
0,020
0,003 e
0,04
0,04
0,04
-
0,34
0,19 h
L 290QS or X42QS
0,14
0,40
1,35
0,020
0,003 e
0,04
0,04
0,04
-
0,34
0,19 h
L320QS or X46QS
0,15
0,45
1,40
0,020
0,003 e
0,05
0,05
0,04
-
0,36
0,20 h
L360QS or X52QS
0,16
0,45
1,65
0,020
0,003 e
0,07
0,05
0,04
g
0,39
0,20 h
L390QS or X56QS
0,16
0,45
1,65
0,020
0,003 e
0,07
0,05
0,04
g
0,40
0,21 h
L415QS or X60QS
0,16
0,45
1,65
0,020
0,003 e
0,08
0,05
0,04
g,i,k
0,41
0,22 h
L450QS or X65QS
0,16
0,45
1,65
0,020
0,003 e
0,09
0,05
0,06
g,i,k
0,42
0,22 h
L485QS or X70QS
0,16
0,45
1,65
0,020
0,003 e
0,09
0,05
0,06
g,i,k
0,42
0,22 h
welded pipe
L245MS or BMS
0,10
0,40
1,25
0,020
0,002 e
0,04
0,04
0,04
-
-
0,19
L290MS or X42MS
0,10
0,40
1,25
0,020
0,002 e
0,04
0,04
0,04
-
-
0,19
L320MS or X46 MS
0,10
0,45
1,35
0,020
0,002 e
0,05
0,05
0,04
-
-
0,20
L360MS or X52 MS
0,10
0,45
1,45
0,020
0,002 e
0,05
0,06
0,04
-
-
0,20
L390MS or X56 MS
0,10
0,45
1,45
0,020
0,002 e
0,06
0,08
0,04
g
-
0,21
L415MS or X60 MS
0,10
0,45
1,45
0,020
0,002 e
0,08
0,08
0,06
g,i
-
0,21
L450MS or X65MS
0,10
0,45
1,60
0,020
0,002 e
0,10
0,08
0,06
g,i,j
-
0,22
L485MS or X70 MS
0,10
0,45
1,60
0,020
0,002 e
0,10
0,08
0,06
g,i,j
-
0,22
a ) Based upon product analysis (see 9.2.4 and 9.2.5) The CEllw limits apply if the carbon mass fraction is greater than 0,12 % and the CEpcm limits apply if the carbon mass fraction is less than or equal to 0,12 %.
b )
For each reduction of 0,01 % below the specified maximum for carbon, an increase of 0,05 % above the specified maximum for manganese is permissible, up to a maximum increase of 0,20 %.
c ) AI total ≤ 0,060 %; N ≤ 0,012 %; AI/N ≥ 2:1 (not applicable to titanium-killed or titanium-treated steel); Cu ≤ 0,35 % (if agreed ,Cu ≤ 0,10 %); Ni ≤ 0,30 %; Cr ≤ 0,30 %; Mo ≤ 0,15 %; B ≤ 0,0005 %.
d ) For welded pipe where calcium is intentionally added, unless otherwise agreed, Ca/s ≥ 1,5 if S > 0,0015 % For SMLS and welded pipes, the calcium concentration shall be ≤ 0,006 %.
e ) The maximum limit for sulfur concentration may be increased to ≤ 0,008 % for SMLS pipe and, if agreed, to ≤ 0,006 % for welded pipe. For such higher-sulfur levels in welded pipe, lower Ca/s ratios may be agreed.
f ) Unless otherwise agreed, the sum of the niobium and vanadium concentrations shall be ≤ 0,06 %.
g ) The sum of the niobium, vanadium and titanium concentrations shall be ≤ 0,15 %.
h ) For SMLS pipe, the listed value may be increased by 0,03.
i ) If agreed, the molybdenum concentration shall be ≤ 0,35 %.
j ) If agreed, the the chromium concentration shall be ≤ 0,45 %.
k ) If agreed, Cr concentration shall be ≤ 0,45 % and Ni concentration shall be ≤ 0,50 %.
Mechanical requirement for Sour Service pipes
Table H.2 ----Requirements for the results of tensile tests
Pipe steel grade
Pipe body of SMLS and welded pipes
Weld seam of HFW and SAW pipes
Yield strength a
Rto,5
Mpa (psi)
Tensile strength a
Rm
Mpa (psi)
Ratio b
Rto,5/Rm
Elongationon 50 mm
or 2 in Af
%
Tensile strength c
Rm
Mpa (psi)
minimum
maximum
minimum
maximum
maximum
minimum
minimum
L245NS or BNS
L245QS or BQS
L245MS or BMS
245
(35 500)
450 d
(65 300) d
415
(60 200)
760
(110 200)
0,93
e
415
(60 200)
L290NS or X42NS
L290QS or X42QS
L290MS or X42MS
290
(42 100)
495
(71 800)
415
(60 200)
760
(110 200)
0,93
e
415
(60 200)
L320NS or X46NS
L320QS or X46QS
L320MS or X46MS
320
(46 400)
525
(76 100)
435
(63 100)
760
(110 200)
0,93
e
435
(63 100)
L360NS or X52NS
L360QS or X52QS
L360MS or X52MS
360
(52 200)
530
(76 900)
460
(66 700)
760
(110 200)
0,93
e
460
(66 700)
L390QS or X56QS
L390MS or X56MS
390
(56 600)
545
(79 000)
490
(71 100)
760
(110 200)
0,93
e
490
(71 100)
L415QS or X60QS
L415MS or X60MS
415
(60 200)
565
(81 900)
520
(75 400)
760
(110 200)
0,93
e
520
(75 400)
L450QS or X65QS
L450MS or X65MS
450
(65 300)
600
(87 000)
535
(77 600)
760
(110 200)
0,93
e
535
(77 600)
L485MS or X70MS
485
(70 300)
635
(92 100)
570
(82 700)
760
(110 200)
0,93
e
570
(82 700)
a For intermediate grades, the difference between the specified maximum yield strength and the specified minimum yield strength shall be as given in the table for the next higher grade, and the difference between the specified minimum tensile strength and the specified minimum yield strength shall be as given in the table for the next higher grade, For intermediate grades, the tensile strength shall be ≤ 760 MPa (110 200 psi).
b This limit applies for pipe with D >323, 9 mm (12.750 in).
c For intermediate grades, the specified minimum tensile strength for the weld seam shall be the same value as was determined for the pipe body using footnote a).
d For pipe with D<219,1 mm (8.625 in), the maximum yield strength shall be ≤495 MPa (71 800 psi).
e The specified minimum elongation, Af, on 50mm or 2 in, expressed in percent and rounded to the nearest percent, shall be as determined using the following equation:
Where
C is 1 940 for calculations using SI units and 625 000 for calculations using USC units;
A xc is the applicable tensile test piece cross-sectional area, expressed in square millimeters (square inches), as follows:
---- for circular cross-section test pieces, 130 mm2 (0.20 in2) for 12,5 mm (0.500 in) and 8,9 mm (0.350 in) diameter test pieces; and 65 mm2 ( 0.10 in2) for 6,4 mm (0.250 in) diameter test pieces;
---- for full-section test pieces, the lesser of a) 485 mm2 (0.75 in2) and b) the cross-sectional area of the test piece, derived using the specified outside diameter and the specified wall thickness of the pipe, rounded to the nearest 10 mm2 (0.01 in2)
---- for strip test pieces, the lesser of a) 485 mm2( 0.75 in2 ) and b) the cross-sectional area of the test piece, derived using the specified width of the test piece and the specified wall thickness of the pipe, rounded to the nearest_10 mm2 (0.01 in2 );
U is the specified minimum tensile strength, expressed in megapascals (pounds per square inch).
H.4.3 HIC/SWC test
The test for evaluation of resistance-to hydrogen- induced cracking shall meet the following acceptance criteria, with each ratio being the maximum permissible average for three sections per test specimen when tested in solution (Environment) A (see ISO 15156-2:2003, Table B.3):
a) crack sensitivity ratio (CSR) ≤ 2 %;
b) crack length ratio (CLR) ≤ 15 %;
c) crack thickness ratio (CTR) ≤ 5 %;
If HIC/SWC tests are conducted in alternative . media (see H.7.3.1.3) to simulate specific service conditions, alternative acceptance criteria may be agreed.
H.4.4 Hardness test
For test pieces subjected to a hardness test (see H.7.3), the hardness in the pipe body, the weld and HAZ shall be ≤ 250 HV10 or 22 HRC (70,6 HR 15N).
The maximum acceptabie hareness of an unexposed weld cap and external surface HAZ and base metal may be 275 HV10 or 26 HRC (73,0 HR 15N) where the equipment user agrees to the alternative weld cap hardness limit, the parent pipe wall thickness is greater than 9 mm, the weld cap is not exposed directly to the sour environment and the escape of hydrogen is not impeded, e.g by cathodic protection.
API 5L Sour Service Line Pipe Comparative Specifications
The information here is summarized from ASTM Standards and API Specification 5L. Please see the specific standards for more information.
PLAIN-END, THREADED-END, BEVELLED-END, SPECIAL COUPLING PIPE
PLAIN-END
TABLE 1
SEAM WELDING
ALL METHODS CONTINOUS WELDING LIMITED TO GRADE A25
ALL METHODS EXCEPT CONTINOUS AND LASER WELDING
TABLE 1
ELECTRIC WELDS: WELDER FREQUENCY
NO MINIMUM
100 KHZ MINIMUM
5.1.3.3.2
HEAT TREATMENTS OF ELECTRIC WELDS
REQUIRED FOR GRADES > X42
REQUIRED FOR ALL GRADES (GR B THROUGH X80)
5.1.3.3.1; J.3.3.2:6.2.7
CHEMISTRY: MAX C FOR SEAMLESS PIPE
0.28% FOR GRADES > GR B
0.24%
TABLES 2A, 2B
CHEMISTRY: MAX C FOR WELDED PIPE
0.26% FOR GRADES > GR B
0.22%
TABLES 2A, 2B
CHEMISTRY: MAX P
0.03%
0.03%
TABLES 2A, 2B
CHEMISTRY: MAX S
ONLY WHEN PURCHASES SPECIFIES SR18
0.02%
TABLES 2A, 2B
CARBON EQUIVALENT
NONE
MAXIMUM REQUIRED FOR EACH GRADE
4.2:4.3:6.1.3: SR15.1
YIELD STRENGTH, MAXIMUM
NONE
MAXIMUM FOR EACH GRADE
TABLES 3A, 3B
UTS, MAXIMUM
NONE REQUIRED
MAXIMUM FOR EACH GRADE
TABLES 3A, 3B
FRACTURE TOUGHNESS
ONLY WHEN PURCHASER SPECIFIES SR4
REQUIRED FOR ALL GRADES
6.2.6; 9.3.5: 9.8.4; 9.10.7;
NON-DESTRUCTIVE INSPECTION OF SEAMLESS PIPES
PERMITTED
SR4 MANDATORY
TABLE 14 9.7.2.6
REPARE BY WELDING OF PIPE BODY, PLATE AND SKELP
PERMITTED BY AGREEMENT
PROHIBITED
5.3.2;9.7.6: B.1;B.2
CERTIFICATION
CERTIFICATES WHEN SPECIFIED PER SR15
PROHIBITED
4.3;9.7.4.4;9.7.6;B.1.2;B.4
TRACEABILITY
TRACEABLE ONLY UNTIL ALL TESTS ARE PASSED UNLESS SR15 IS SPECIFIED
CERTIFICATES (SR15.1) MANDATORY
TRACEABLE AFTER COMPLETION OF TESTS (SR15.2) MANDATORY
12.1
5.6
CHEMICAL REQUIREMENTS FOR API 5L Sour Service steel Pipe
API 5L Specifications covers seamless and welded pipe suitable for use in conveying gas, water, oil, and other liquefied media. The attached requirements cover our offering of API 5L 45th Ed, PSL 1 Seamless and Welded;
API 5L 45th Ed PSL 2 Seamless & Welded; and API 5L 45th Ed PSL2 Welded only.
TENSILE PROPERTIES FOR SEAMLESS AND WELDED API 5L Sour Service steel Pipe
tensile properties data for seamless and welded API 5L steel pipe API 5L 45th Ed PSL 1, PSL 2.
TESTING REQUIREMENTS FOR SEAMLESS AND WELDED API 5L Sour Service steel Pipe
Our API 5L Seamless Pipes hydrostatic and mechanical testing information for all sizes and grades covered by the specification.
PERMISSIBLE VARIATIONS FOR SEAMLESS AND WELDED API 5L Sour Service steel Pipe
Grade A, B, A25
X42 through X80
NPS 2-1/2 and smaller -- Seamless and welded, %
+20 -- 12.5
+15 -- 12.5
NPS 3 -- Seamless and welded, %
+18 -- 12.5
+15 -- 12.5
NPS 4 through 18 -- Seamless and welded, %
+15 -- 12.5
+15 -- 12.5
NPS 20 and larger -- Welded, %
+17.5 -- 10.0
+19.5 -- 8.0
NPS 20 and larger -- Seamless, %
+15.0 -- 12.5
+17.5 -- 10.0
Marking Requirements
Paint-stenciled or die-stamped manufacturer’s name or mark, Spec 5L, size, weight per foot, grade, process of manufacture, type of steel, length (NPS 4 and larger only). Test pressure when higher than tabulated
(NPS 2 and larger only).
Supplemental Annexes for API 5L Sour Serviceseamless and welded steel Pipe
API Specification 5L contains 15 Supplemental Annexes that address special conditions and/or additional requirements.
API 5L LINE PIPES OF TOP APPROVED COMPANIES
Sabic Saudi Arabia)
Saudi Aramco(Saudi Arabia)
ALBA (Saudi Arabia)
QAFCO(Qatar)
Maaden(Saudi Arabia)
KNPC(Kuwait)
Kuwait Oil Company(Kuwait)
Qatar Petroleum(Qatar)
Petroleum Development Oman(Oman)
ADNOC(United Arab Emirates)
Orpic(Oman)
Takreer(Abu Dhabi)
YASREF(Abu Dhabi)
Petrobras(Braizl)
Petronas(Malaysia)
NIOC(Iran)
NPDC(Nigeria)
Egyptian General petroleum Corporation(Egypt)
API 5L Sour Service Seamless Line Pipe in various Grades Available in Ex-Stock warehouse
WE MAINLY STOCK & SUPPLY THE API-5L GRADE-B, X42, X46, X52, X56, X60, X65, X70, X80 Sour Service LINE PIPE SEAMLESS PIPE OF FOLLOWING MAKE:
API 5L GRADE B, x42,x46,x52,X56,x56,x60,x70 Sour Service Carbon Steel Seamless Pipe Sizes Available in Stock with Price
Available Grade of API 5L Sour Service Seamless Pipes in Carbon Steel in Ready Stock -
We Export API 5L X42,X46,X52,X56,X60,X65,X70 Pipes -
SUPPLYING API 5L SOUR SERVICE PIPES TO COUNTRIES -
We Export API 5L Sour Service Seamless Pipe to Saudi Arabia, Iran, Iraq, United Arab Emirates, Qatar, Bahrain, Oman, Kuwait, Turkey, Egypt, Yemen , Syria, Israel, Jordan, Cyprus, Singapore, Malaysia, Indonesia, Thailand, Vietnam, South Korea, Japan, Sri Lanka, Maldives, Bangladesh, Mayanmar, Taiwan, Cambodia, Argentina, Bolivia, Brazil, Chile, Venezuela, Colombia, Ecuador, Guyana, Paraguay, Uruguay, United States Of America, Canada, Mexico, Panama, Costa Rica, Puerto Rica, Trinidad And Tobago, Jamaica, Bahamas, Denmark, Russia, Norway, Germany, France, Italy, United Kingdom, Spain, Ukraine, Netherland, Belgium, Greece, Czech Republic, Portugal, Hungary, Albania, Austria, Switzerland, Slovakia, Finland, Ireland, Croatia, Slovenia, Malta, Nigeria, Algeria, Angola, South Africa, Libya, Egypt, Sudan, Equatorial Guinea, The Republic Of Congo, Gabon, Europe, Africa, Asia, North America, South America, Middle East, Far East.etc
MAH Metal Inc. is a well known worldwide exporter of API 5L Sour Service Seamless Pipe, MAH Metal Inc. is committed to provide each and every customer with the highest standard of customer service. We deals in API 5L Sour Service Seamless Pipe in India and Overseas, offering a wide range of API 5L Sour Service Seamless Line Pipes
sour service material selection, what is sour service in oil and gas, sour service requirements, sour service line pipe, sour service pipeline, material selection for sour service environment, what is non sour service in oil and gas, sour service wiki, API 5L X42, X46, X52, X56, X60, X65, X70 PIPE
API 5L Sour Service Pipe, SOUR Service Pipe, SOUR Service Line Pipes
We provide API 5L SOUR Service Pipe in Grade B, X42, X46, X52, X56, X60, X65 with PSL1 and PSL2. We Carry Complete Range from 3/8" NB to 24" NB, wall Thickness upto 200 MM. Prosaic Steel and Alloys API 5L Grade B Pipe are known for its High Quality and Competitive Price.
Supplying Steel Pipes and Tubes Approved by ONGC, RELIANCE, RIL, BPCL, HPCL, BHEL, CAIRN ENERGY, NAGARJUNA CORPORATION, KNPC, INOC, SAUDI ARAMCO, SABIC, SOCAR, RASGAS, QATAR PETROLEUM, PEMEX, GASCO, ADOS, BP, BRITISH PETROLEUM, POGC, PDO, SHELL, EXXONMOBIL, PETRONAS, PETROBRAS, KOC, OXY, SINOPEC, TOTAL SA, CHEVRON, PDVSA, PTT, CONOCO PHILLIPS, STATOIL ASA, ROYAL DUTCH SHELL, LUKOIL, SUNCOR ENERGY, NNPC, DOOSAN, CNPC, PERTAMINA, ARMO, GS CALTEX, S-OIL, SK ENERGY, PETROTRIN etc
Leading Exporter of Steel Pipe & Tubes to Leading Exporter of Pipe & Tubes to Saudi Arabia, Iran, Kuwait, Iraq, Oman, Qatar, Azerbaijan, United Arab Emirates, Bahrain, Turkey, Jordan, Indonesia, Singapore, Malaysia, Vietnam, Philippines, Thailand, South Korea, Laos, Cambodia, Japan, Nigeria, Egypt, South Africa, Algeria, Morocco, Angola, Sudan, Ethiopia, Kenya, Tunisia, Ghana, Libya, Uganda, The Republic of Congo, Equatorial Guinea, Gabon, Senegal, Niger, Cameroon, Chad, Trinidad and Tobago, Brazil, Mexico, Venezuela, Cambodia, Chile, Peru, United States of America, Canada, Netherlands, Spain, United Kingdom, Germany, Italy, Albania, France, Russia, Ukraine, Hungary, Norway, Poland, Bangladesh, Sri Lanka, Maldives, Australia, New Zealand etc.